Noise Reduction Coating factory

Product introduction: AMMT-DP100 high-performance viscoelastic damping coating material is a special material that can effectively reduce the vibration of the equipment and prevent the spreading of noise. The material uses the constraint damping structure, including free damping coating material and restraint damping material. The free damping coating material is a polyurethane material of blade-coating type without solvent. The product is of two-component, and component A is isocyanate prepolymer, and B is the mixture of polyether polyol, chain extender and functional filler. Restraint damping material is a kind of epoxy resin material of blade-coating type. The material is composed of two components. Component A is mixed of epoxy resin and filler, while B is amine hardener. It forms the constraint damping complex structure with free damping coating material. Features: The damping temperature range is wide and the loss factor is high. In the temperature range of 60鈩?(-10-50鈩?, the free loss factor is 0.7-2.2; the complex loss factor is 0.13. High fire resistance: Oxygen index of material: 37%; the complex coating meets the demand of the flammability test (low flame spread) on the surface of the facing material of the 2010 International Code for Application of Fire Test Procedures of International Marine Organization. High safety: Meeting the demand of GJB11A-1998 (90 days) toxicity test Excellent anti-corrosion performance: The constraint damping complex coating is of good performances such as salt-spray resistance, acid and alkali resistance, oil resistance, seawater resistance, and hot-wet resistance. It is suitable for various corrosion environments such as ocean and industrial air environments. Main performance indexes: PerformancePerformance indexTest standard Free loss factor0.7-2.2 (temperature range: -10-50鈩?GB/T16406 Complex loss factor0.13GB/T16406 Oxygen index %37GB/T10707 Low flame spread characteristicsMeeting the requirementInternational Code for Application of Fire Test Procedures ToxicityMeeting the demand of GJB 11A-1998 (90 days)GJB 3881 Salt fog resistance5000hGB/T1771 Seawater resistant (room temperature)6 monthsGB/T5776 Resistant to nuclear radiationNo obvious change in appearance after 1脳105GyJJF 1080 Adhesive force鈮?MPaGB/T5210 Application: High-performance viscoelastic damping coating material is widely used for vibration and noise reduction in the fields of the ship and ocean engineering and the mechanical equipment for its excellent damping capacity, such as marine engine room, command room, rest room and meeting room as well as the base of mechanical equipment. Construction process: Heavy duty primer: Product parameters: Color: Grey (adjustable) Mixing ratio: A: B=5: 1 (mass ratio) Specific weight: approx. 1.66脳103kg/m3 Solid content (%): 鈮?8 Constructional equipment: High-pressure airless spraying equipment and spray gun are used for spraying, the type of main engine is Graco X-60 and the type of spray gun is Graco XTR-7. Parameter setting: Pressure setting 2,000-3,000psi. Drying time Ambient temperature/鈩?/p>10203040 Surface dry time /h43.2532.5 Hard dry time /h15131211 Note: Relative humidity 60% Damping coating material: Product parameters Color: Lemon yellow (adjustable) Mixing ratio: A: B=1:1.8 (mass ratio) Specific weight: approx. 1.38脳103kg/m3 Solid content (%): 鈮?8 Constructional equipment Pistol drill with a caliber of 15mm (1,000w at least), stirring rod with a caliber of 12mm (6-blade paddle), 4-cun and 2-cun putty knives and other tools for blade coating construction. Drying time Ambient temperature/鈩?/p>10203040 Surface dry time /h10643.5 Hard dry time /h24181211 Note: Relative humidity 60% Constraint damping decoupling material: Product parameters: Color: Sky blue (adjustable) Mixing ratio: A: B=4: 1 (mass ratio) Specific weight: approx. 1.46脳103kg/m3 Construction tools Scraper, scraper blade and other tools for blade coating construction. Drying time Ambient temperature/鈩?/p>10203040 Surface dry time (h)5432 Hard dry time (h)9864 Note: Relative humidity 60% Mating scheme: AMMT-DP100 high-performance viscoelastic damping coating material The high-performance viscoelastic damping coating is composed of damping layer and constraint layer. Firstly, it's necessary to blade coat the damping layer on the substrate with antiseptic treatment, with the theoretical thickness of the damping layer being as 1mm; the remain part is the constraint layer; the thickness of the whole coating is suggested to be 1.5 to 2 times of that of the substrate.Noise Reduction Coating factory website:http://www.ammtchina.com/noise-reduction-coating/